PROBOND UltraFR® is a Fire Resistant Aluminium Cladding panel, ideal for all RV & Marine Transport applications.

The mineral core is engineered to withstand intense heat without burning, while the outer aluminium layer is coated with PPG FEVE for prolonged outdoor resilience against Australia’s harsh UV exposure. This fire resistant aluminium cladding panel sets the benchmark for all signage, RV and Marine applications, offering top-tier durability.

Safety First

Designed to achieve a Group1 BCA Classification, PROBOND UltraFR® panels are ideal for exterior and interior flat-face signage, shop fitouts, various displays, RVs, and Marine applications, especially those necessitating fire-resistant properties.

Versatility

PROBOND UltraFR® panels are 3mm thick and have a 0.3mm aluminium skin. Their versatility allows for folding, grooving, and CNC routing, and they can be efficiently cut using standard aluminium blades via guillotine or sawing methods.

PROBOND UltraFR® comes in an extensive array of colours and surface finishes*, offering exceptional evenness and rigidity.

* Test results available on request.

Download product overview Book a Consultation

fire resistant aluminium cladding - PROBOND

Colour options

Gloss White

Matt White

Panel Properties

Panel Thickness (mm)	3mm
Skin Thickness (mm)	0.30mm
Weight (kg/m2)	5.0kg
Sound Absorption	0.05
Sound Attenuation	24
Water Absorption % by Volume	0.01
Thermal Performance R Values	0.008
Core Composition	> 75% Magnesium Hydroxide(Mg(OH)2) - Fire Resistant
Fire Performance	Group 1 according to AS ISO 9705:2003
Tensile Strength of Aluminium Layers	50 MPa

Dimensional Tolerances

Panel Thickness (mm)	3 mm
Width (mm)	-0 +2 (+/- 0.2)
Length (mm)	-0 +3 (+/- 0.2)
Diagonal	-0 +5 (+/- 0.2)
Thermal Expansion	2.4mm/m @100°C temp difference
Aluminium Thickness	0.30 mm

Surface Properties

Paint Thickness (microns)	26±1μm
Pencil Hardness	2H
Toughness of Coating	≤2T
Temperature Resistance	-50℃ -80℃
Impact Strength (kg/CM2)	50kg/cm2. No crack
Boiling Water Resistance	Boiling for 2h without change
Acid Resistance	Immerse surface with 5%HCI(v/v) for 24H without change
Alkali Resistance	Immerse surface with 5%NaOH(m/m) for 24H without change
Oil Resistance	Immerse surface with 20# engine oil for 24H without change
Solvent Resistance	Clean 100 times with Methyl Ethyl Ketone (MEK) without change
Peel Strength	7.0N/mm