PROBOND UltraFR® is one of the only Fire Resistant Signage Grade panels in the world

PROBOND UltraFR® is designed for where a fire-resistant panel with a Group1 BCA Classification is required for signage applications.*

The mineral core is designed to resist burning under extreme fire conditions and the external aluminium has a PPG FEVE Coating for extended outdoor durability designed to withstand the harsh Australian UV conditions. It is the highest standard of panel for all signage applications.

PROBOND UltraFR® has a total thickness of 3mm and an aluminium skin thickness of 0.3mm. It is suitable for folding, grooving and CNC routing and can be guillotine cut or sawn using standard aluminium blades. Available in white, it offers exceptional flatness and rigidity. Ideal for both exterior and interior flat face signage, shop fitouts, and display applications, especially where fire-resistant properties are essential.

*Test results available on request.

Download product overview Book a Consultation

ACP Panel Board - Cladding Panel - cladding panel - aluminium cladding panels - PROBOND

composite panelling - panel aluminium - PROBOND

fire resistant aluminium cladding - aluminium composite panel 3mm - PROBOND

Colour options

Gloss White

Matt White

Panel Properties

Panel Thickness (mm)	3mm
Skin Thickness (mm)	0.30mm
Weight (kg/m2)	5.0kg
Sound Absorption	0.05
Sound Attenuation	24
Water Absorption % by Volume	0.01
Thermal Performance R Values	0.008
Core Composition	> 75% Magnesium Hydroxide(Mg(OH)2) - Fire Resistant
Fire Performance	Group 1 according to AS ISO 9705:2003
Tensile Strength of Aluminium Layers	50 MPa

Dimensional Tolerances

Panel Thickness (mm)	3 mm
Width (mm)	-0 +2 (+/- 0.2)
Length (mm)	-0 +3 (+/- 0.2)
Diagonal	-0 +5 (+/- 0.2)
Thermal Expansion	2.4mm/m @100°C temp difference
Aluminium Thickness	0.30 mm

Surface Properties

Paint Thickness (microns)	26±1μm
Pencil Hardness	2H
Toughness of Coating	≤2T
Temperature Resistance	-50℃ -80℃
Impact Strength (kg/CM2)	50kg/cm2. No crack
Boiling Water Resistance	Boiling for 2h without change
Acid Resistance	Immerse surface with 5%HCI(v/v) for 24H without change
Alkali Resistance	Immerse surface with 5%NaOH(m/m) for 24H without change
Oil Resistance	Immerse surface with 20# engine oil for 24H without change
Solvent Resistance	Clean 100 times with Methyl Ethyl Ketone (MEK) without change
Peel Strength	7.0N/mm